Effects of UV and white light illuminations on photosensing properties of the 6,13-bis(triisopropylsilylethynyl)pentacene thin film transistor

Abstract

The effects of UV and white light illuminations on the electrical and photosensing properties of the 6,13-bis(triisopropylsilylethynyl)pentacene thin film transistor were investigated. The photosensitivity (I ph/I dark) values of the transistor in the OFF state were found to be 1.156 and 2.12 under UV 365 nm (for V g = -10 V) and white light illuminations (for V g = -10 V and P = 100 mW/cm 2), respectively. The threshold voltage value of the TIPS-pentacene transistor was shifted from a smaller (0.215 V) value to higher (1.095 V) value with UV illumination, while it was shifted from a negative value (-1.29 V) to positive value (0.525 V) with white light illumination. The mobility ? value (3.412 × 10 -2 cm 2/Vs) of the TIPS-pentacene transistor under dark is lower than that of the values under UV and white light illuminations. The sub-threshold swing value under dark is higher than that of under UV and white light illuminations. The interface trap density of the TIPS-pentacene transistor is decreased with increasing illumination. The lowest D it value (0.941 × 10 13 eV -1 cm -2) of the TIPS-pentacene transistor causes the highest mobility (6.322 × 10 -2 cm 2/Vs). The photoresponsivity R values of the TIPS-pentacene transistor vary from 11.58 mA/W to 53.48 mA/W. © 2012 Elsevier B.V.